Polymaker PolySonic High Speed Printing PLA PRO 3D Printer Filament 1KG 1.75mm

Polymaker PolySonic High Speed Printing PLA PRO 3D Printer Filament 1KG 1.75mm

Black (HEX Code - ⌗080A0D
$28.99
$28.99
Skip to product information
Polymaker PolySonic High Speed Printing PLA PRO 3D Printer Filament 1KG 1.75mm
  • Polymaker PolySonic High Speed Printing PLA PRO 3D Printer Filament 1KG 1.75mm
  • Polymaker PolySonic High Speed Printing PLA PRO 3D Printer Filament 1KG 1.75mm
  • Polymaker PolySonic High Speed Printing PLA PRO 3D Printer Filament 1KG 1.75mm
Polymaker PolySonic High Speed Printing PLA PRO 3D Printer Filament 1KG 1.75mm

Polymaker PolySonic High Speed Printing PLA PRO 3D Printer Filament 1KG 1.75mm

$28.99
$28.99

PolySonic PLA Pro 3D printer filament delivers exceptional strength and durability with the capability to print at incredible speeds up to 300mm/s. This advanced PLA filament formulation provides impact strength similar to ABS and bending strength that outperforms ASA and PETG, making it ideal for functional parts when time is critical. Perfect for users who need tough, reliable prints without compromising on speed or quality.

Specification Value
Filament Diameter 1.75mm
Spool Weight 1kg
Print Temperature (Classic) 190–230°C
Print Temperature (High Speed) 210–230°C
Bed Temperature 25–60°C
Print Speed (Classic) 50–100mm/s
Print Speed (High Speed) 100–300mm/s
Maximum Flow Rate 24mm³/s
Layer Adhesion 31.9–33.6 MPa
Tensile Strength 39.3–41.2 MPa
Impact Strength 19.4–22.7 kJ/m²
Retraction Distance (Direct Drive) 1mm
Retraction Speed (Direct Drive) 20mm/s
Retraction Distance (Indirect Drive) 3mm
Retraction Speed (Indirect Drive) 40mm/s
Drying Settings 55°C for 6 hours
Spool Inner Hole Diameter 55±1mm
Spool Diameter 200±1mm
Spool Width 65.6±2mm
Empty Spool Weight 140±7g

Best For:

  • High-speed 3D printing applications requiring fast turnaround times
  • Functional prototypes and end-use parts that need durability
  • Production environments where throughput and quality are critical
  • Parts requiring impact resistance similar to ABS with easier printing
  • Projects needing strong layer adhesion and mechanical properties
  • Users with high-performance extruders capable of high flow rates

Related products